Concrete panel board

ABSTRACT

A concrete panel board is provided. The panel board includes: a substrate board; a primer layer applied to the substrate; a thinset mortar layer applied to the primer layer; a plaster layer applied to the thinset mortar layer; and a sealant layer applied to the plaster layer.

TECHNICAL FIELD

This invention relates to concrete panel boards and related methods ofmanufacture.

BACKGROUND

The popularity of the “industrial look” in interior design has led to arise in the use of concrete. A disadvantage of traditional concrete wallpanels is their heavy weight. Heavy panels are costly to transport anddifficult to erect or mount. Also, traditional concrete wall panels aredifficult to cut not only due to their hardness but also because theygenerate a significant amount of dust, which is harmful to health. Thereis a general desire to provide concrete panels that are lightweight andeasy to cut.

DESCRIPTION

Throughout the following description specific details are set forth inorder to provide a more thorough understanding to persons skilled in theart. However, well known elements may not have been shown or describedin detail to avoid unnecessarily obscuring the disclosure. Accordingly,the description is to be regarded in an illustrative, rather than arestrictive, sense.

One aspect of the invention provides a concrete panel board. Theconcrete panel board of the present invention is economical,lightweight, durable and versatile, and can be readily provided in avariety of colors and textures. The board simulates the appearance, feeland durability of panels formed entirely from concrete. The board hasother advantages such as heat and water resistance making it suitablefor use in a variety of different building and finishing applications.For example, the board may be used as a finish for any interior designpurpose, including but not limited to fireplace surrounds, backsplashes,ceilings, bulkheads, hallways, corridors, feature walls, accent walls,columns, lobbies, furniture and the like. In some embodiments, theconcrete panel board may be used for exterior design purposes.

In some embodiments, the concrete panel board includes a substrate, aprimer layer, a thinset mortar layer, a plaster layer and a sealantlayer.

The substrate may be any rigid board material such as those suitable foruse in sheathing. Examples of suitable substrates include engineeredwood board, plywood board, gypsum board, polyisocyanurate board,polystyrene board, magnesium oxide board and the like. In particularembodiments, the magnesium oxide board may include magnesiumoxychloride, perlite, a reinforcing mesh material and wood dust. In someembodiments the magnesium oxide board may be silica dust free.

The substrate may be provided at a thickness of ¼″ or ½″, for example.In other embodiments, the substrate may be thinner or thicker dependingon the application. Generally the substrate is planar but in someembodiments may be curved or any other shape.

The primer layer may be any preparatory coating that facilitates bettersubsequent adhesion of the thinset mortar layer. In some embodiments theprimer layer may be a water-based styrenated acrylic. The inventor hasdetermined that the primer layer ensures the substrate is sealed forbetter cutting, strengthened against cracking under heat, and adds alayer of water resistance. The primer layer also facilitates applicationof the thinset mortar layer since it makes the substrate less absorbent.

The thinset mortar layer is a layer of thinset mortar, also known asthinset cement, dryset mortar and drybond mortar. The properties ofthinset mortar are set out in the A118.1 specification of the AmericanNational Standards Institute. Thinset mortar is a mixture of cement,sand, a water retention compound, and water. The cement will preferablybe portland cement, although other inorganic cements, such as thosecomprising gypsum or calcium aluminate, may also be used. The thinsetmortar layer may be reinforced with microfibers and may be polymermodified.

In some embodiments, the thinset mortar layer may be provided at athickness of about 1/16″ to about ¼″, or about ⅛″. In other embodiments,the thinset mortar layer may be thinner or thicker depending on theapplication. A colourant may be added to the thinset mortar layer. Thecolourant may be a 50/50 mixture of black and white colourant. Thecolourant may be a mixture of other colourants.

The plaster layer may be lime plaster, gypsum plaster or cement plaster.In some embodiments, the plaster layer may be applied to a thickness of⅛″. In other embodiments, the plaster layer may be thinner or thickerdepending on the application. Lime plaster is a preferred plaster, andis essentially pure ground limestone. In some embodiments, only a singlelayer of lime plaster is applied.

In some embodiments, the thinset mortar layer is thicker than theplaster layer. In particular embodiments, the ratio of thinset mortar toplaster is about 70:30, or about 60:40, or about 50:50. The ratio maydepend on the application method and the specified desired finish.

A colourant may be added to the plaster layer. The colourant may be a50/50 mixture of black and white colourant, to achieve the grey colourof concrete. The colourant may be mixtures of other colourants toachieve other colour values.

The sealant layer may be any sealant capable of sealing the layers fromthe environment. In some embodiments, one to three layers of sealant maybe applied depending on the application. In some embodiments the sealantmay comprise acrylic varnish.

In some embodiments the concrete panel board may be fire resistant,water resistant, and mold resistant, in accordance with thespecifications of the substrate, such as magnesium oxide board. Inembodiments where the concrete panel board need not be fire resistant,and for example only water resistant and mold resistant, a substratesuch as polyisocyanurate board or polystyrene board may be used.

In some embodiments, the concrete panel board may be applied to plywood,MDF, drywall, concrete board, concrete, metal, glass and the like.

Due to the thin layer of concrete of the finished concrete panel board,the board is significantly lighter than a concrete panel of equivalentsize. The thinness of the concrete layer also makes cutting operationseasier, with minimal concrete dust being generated.

The shape, size, and weight of the finished concrete panel board canvary greatly depending on the particular application for which the boardis used. However, it is an object of the present invention to provide aconcrete panel board that is significantly lighter than traditionalconcrete panel boards. For example, in some embodiments when using a ½″magnesium oxide board as a substrate, the concrete panel board will havea weight in the range of about 2.0 to about 3.0 pounds per square feet,or about 2.4 to about 2.7 pounds per square feet. In other embodimentswhen using a ½″ polyisocyanurate board or polystyrene board as asubstrate, the concrete panel board will have a weight in the range ofabout 1.0 to about 2.0 pounds per square feet.

Another aspect of the invention relates to making a concrete panel boardas described herein. In each of the steps of manufacture, the layersapplied to the substrate may be troweled, brushed, or sprayed on.

After ensuring that the surface of the substrate is clean and dry, aprimer layer is applied to one or both surfaces of the substrate. Theprimer layer is then dried on the board for about an hour at roomtemperature. Drying time may be longer or shorter depending on thetemperature; for example a controlled heat environment may significantlyreduce the drying time. Once dried, the primer layer provides a readilyadhesive surface for the next, thinset mortar layer.

In some embodiments the surface of the substrate may be prepared foroptimal bonding before the application of the primer layer, by forexample etching, sanding or other techniques known in the art.

After the primer layer is applied and dried, mortar is prepared bymixing a dry mortar mix with water. In some embodiments, 2 parts of drymortar mix may be combined with 1 part water, by volume, and mixed witha powered mixing paddle. Colourant may be added at this stage as well.To achieve the grey appearance of concrete, a 50/50 blend of black andwhite colourant, or other colourant may be added, for example, and mixedinto the mortar.

A thin layer of mortar is applied to the primed surface of the board.The layer of mortar may be applied at a thickness of about 1/16″ toabout ¼″, or about ⅛″. The thinset mortar layer is then allowed to dryfor about 6 hours at room temperature. Again, drying time may be longeror shorter depending on the temperature.

After the thinset mortar layer is applied and dried, plaster is preparedby mixing with water. Colourant may be added at this stage as well. Theplaster may be applied at a thickness of about 1/16″ to about ¼″ orabout ⅛″. Different troweling, brushing, or spraying strokes may be usedto introduce subtle colour variations in the plaster layer, and in someembodiments to create the “distressed” concrete appearance.

In some embodiments, before the plaster layer sets, wet sandpaper may bestroked over the surface of the plaster to help emulsify the plaster. Insome embodiments, sandpaper of 100 grit to 220 grit, or 150 grit, may beused. Again, different strokes of application may be used to create theaesthetics of the concrete. In some embodiments, wood is applied to thesurface to create wood grain finishes. The plaster layer is allowed todry for 2 to 3 hours at room temperature. Again, drying time may belonger or shorter depending on the temperature.

Lastly, sealant is applied after the plaster is applied and dried. Thenumber of coats of sealant applied depends on the application of theconcrete panel board. Applications where moisture will be present mayrequire a greater number of coats of sealant, for example.

Another aspect of the invention relates to providing the materialsrequired to form the concrete panel board according to embodiments ofthe invention as a kit. Such materials can be pre-mixed, or can besupplied for mixing by the user. The kit can also include containers formixing and storing the thinset mortar layer and the plaster layer, aswell as means for applying the layers to the substrate, such as atrowel, brush or sprayer. The kit can also include a written instructionleaflet explaining how to make and use the concrete panel board inaccordance with the embodiments of the invention.

The preferred forms of the invention described above are to be used asillustration only, and should not be used in a limiting sense tointerpret the scope of the present invention. Obvious modifications tothe exemplary embodiments, set forth above, could be readily made bythose skilled in the art without departing from the spirit of thepresent invention.

1. A concrete panel board comprising: a substrate board; a primer layerapplied to the substrate; a thinset mortar layer applied to the primerlayer; a plaster layer applied to the thinset mortar layer; and asealant layer applied to the plaster layer.
 2. A concrete panel boardaccording to claim 1 wherein the substrate board is selected from thegroup consisting of engineered wood board, plywood board, gypsum board,polyisocyanurate board, polystyrene board and magnesium oxide board. 3.A concrete panel board according to claim 2 wherein the magnesium oxideboard comprises magnesium oxide and perlite.
 4. A concrete panel boardaccording to claim 1 wherein a thickness of the substrate board is ¼″ or½″.
 5. A concrete panel board according to claim 1 wherein the primerlayer comprises an acrylic primer.
 6. A concrete panel board accordingto claim 1 wherein the thinset mortar layer comprises fiber reinforcedmortar.
 7. A concrete panel board according to claim 1 wherein athickness of the thinset mortar layer is about ⅛″.
 8. A concrete panelboard according to claim 1 wherein the plaster layer is selected fromthe group consisting of gypsum plaster, lime plaster and concreteplaster.
 9. A concrete panel board according to claim 8 wherein theplaster layer comprises lime plaster.
 10. A concrete panel boardaccording to claim 1 wherein a thickness of the plaster layer is about⅛″.
 11. A concrete panel board according to claim 1 wherein the sealantlayer comprises an acrylic varnish.
 12. A concrete panel board accordingto claim 1 wherein the one or more of the thinset mortar layer and theplaster layer comprise a colourant.
 13. A method of making a concretepanel board comprising: a. providing a substrate; b. applying a primerlayer to the substrate; c. drying the board after step b; d. applying athinset mortar layer to the primer layer; e. drying the board after stepd; f. applying a plaster layer to the thinset mortar layer; g. dryingthe board after step f; and h. applying a sealant layer to the plasterlayer.
 14. A method according to claim 13 wherein in step a thesubstrate comprises an engineered wood board, plywood board, gypsumboard, polyisocyanurate board, polystyrene board or magnesium oxideboard.
 15. A method according to claim 13 wherein step d comprisingapplying a ⅛″ layer of fiber reinforced mortar.
 16. A method accordingto claim 13 wherein the step f comprising applying a ⅛″ layer of limeplaster;
 17. A method according to claim 13 wherein a colourant is addedat step d and/or step f.
 18. A method according to claim 13 wherein wetsandpaper is applied between step f and g to enhance emulsification ofthe plaster layer.
 19. A method according to claim 13 wherein step hcomprises applying an acrylic varnish.
 20. A method according to claim13 wherein step h comprises applying 1 to 3 coats of the sealant layer.21. A method according to claim 13 wherein between steps f and g a woodform is applied to the plaster layer to create a wood grain finish.